| Tape Name | Model | Specifications |
| Polyimide tape | SLK2560ESD | 0.06*500mm*33m |
Polyimide tape SLK2560ESD Description:
● SLK2560ESD polyimide tape with release film laminating
● mold sections made according to customer requirements
SLK2560ESD polyimide films (Polyimide) The coated substrate of high temperature resistant silicone pressure sensitive adhesive.
Product composition:
→ polyimide film
→ silicone pressure sensitive adhesive
→ special structure conductive layer
Physical parameters:
| Project | Unit | Specification | Value Test Method | Remark |
| Color | Amber | Visual | ||
| Substrate thickness | mm | 0.025 | ASTM D-3652 | ±0.001mm |
| The total thickness | mm | 0.06 | ASTM D-3652 | ±0.002mm |
| Density | g/cm3 | 1.42 | ASTM D-1505 | |
| Tensile strength | Kg/mm2 | 29(MD);30(TD) | ASTM D-882 | |
| Elongation at break | % | 127(MD);122(TD) | ASTM D-882 | |
| Heat shrinkage (200 ℃ * 2HR) |
% | 0．09 MD 0．02 TD |
IPC TM650 2．2．4A |
|
| Coefficient of thermal expansion |
Ppm/℃ | 35(MD);34(TD) | TMA Method | 100~200℃ |
| Surface resistivity | Ω | 10个8次方 | ESD S-11 |
Features:
With high electrical strength, high temperature, high adhesion, H-class insulation and corrosion resistance, soft docile, then tear off without leaving adhesive residue and other features.
Application areas:
Can be used for power switches, motors, relays, cables, coils, capacitors and lithium batteries, SMT surface mount transformer manufacturing.
Storage conditions and validity:
1. The product is stored at room temperature, 20 ~ 80% RH environment.
2. Use the product within six months after the date of manufacture, get the best performance.
Note:
All above-mentioned techniques are the company uses proven and reliable testing methods, average values obtained after repeated testing. However, to ensure the correct selection and use of our products, please use the object based on desire, first using a detailed understanding of the purpose and conditions of probation, or notify the Company in order to provide you with further explanation and service.